Poliuretan elastomer formed by the polymerization reaction of diisocyanate and active hydrogen compound, the rigid segment containing urea group composed of diisocyanate and diamine chain extender, the glass transition temperature is much higher than room temperature, and it is glassy at room temperature. Subcrystals or microcrystals form the plastic phase; flexible segments of polyether or polyester are gathered together to form the matrix or matrix of the poliuretan rubber. Because its glass transition temperature is lower than room temperature, it is called the rubber phase. The microphase separation of the poliuretan elastomer makes the poliuretan elastomer have the advantages of good wear resistance, wide range of hardness, high strength and high elongation, large load supporting capacity, good shock absorption effect and excellent oil resistance. Choosing a suitable molding and processing method can maximize the performance of poliuretan elastomers and prepare various poliuretan elastomers with excellent properties, which are widely used as plastics, rubber, fibers, adhesives and coatings, and even as functional polymer materials. Such as medical poliuretanbahan.
1.1 Prinsip umum untuk memilih metode pemrosesan pembentukan
(1) Proses pencetakan biasanya untuk melelehkan atau mengubah bentuk senyawa polimer dalam keadaan padat (bubuk atau granular), pasta atau larutan, dan membentuk bentuk yang diinginkan melalui cetakan, dan mempertahankan bentuk yang telah diperoleh, dan akhirnya mendapatkan produk. proses kerajinan.
(2) Alur pemrosesan pencetakan umum: â‘ Metode pembentukan campuran senyawa polimer sekali dan dua kali untuk menghasilkan produk; â‘¡Metode pembentukan senyawa polimer untuk menghasilkan produk sekaligus; â‘¢Metode produksi produk dari campuran monomer dalam satu langkah â‘£ Metode produksi satu langkah dari campuran oligomer.
(3) Kinerja pemrosesan dan faktor-faktor yang mempengaruhinya: â‘ Kemampuan untuk meremas, dalam ekstruder, laras mesin injeksi, rol kalender, dan cetakan, ketika material dideformasi oleh ekstrusi, bentuk material diperoleh dan kemampuan yang terjaga. Faktor pembatasnya: viskositas leleh, struktur peralatan pemrosesan, reologi leleh, dan laju aliran leleh. â‘¡Moldability, dalam proses pencetakan di bawah aksi mesin injeksi, ekstruder, dan mesin kompresi, material terdeformasi di bawah aksi suhu dan tekanan dan kemampuan untuk dicetak dalam cetakan. Faktor pembatasnya: reologi, sifat termal dan sifat fisik dan mekanik lainnya dan reaktivitas kimia senyawa polimer. â‘¢Extensibility, dalam calendering atau peregangan, bahan berubah bentuk dengan calendering atau peregangan dalam satu atau dua arah. Faktor pembatasnya: plastisitas material dan efek pengerasan regangan. â'£ Spinnability, nozzle selama pencetakan ekstrusi, kemampuan material untuk membentuk serat padat terus menerus melalui pencetakan. Faktor pembatasnya: reologi, viskositas dan kekuatan leleh, stabilitas termal dan stabilitas kimia.
1.2 Prinsip umum untuk memilih metode pencetakan dan pemrosesan untukpoliuretanelastomer
Poliuretan elastomer molding processing system is divided into liquid system and solid system. On the basis of the rapid polymerization reaction of diisocyanate and active hydrogen compound, the molding processing method is conducive to the microphase separation of the poliuretan elastomer. , Liquid system, poliuretan casting glue can be processed by casting (manual casting, centrifugal casting and vacuum casting), reaction injection molding, spraying, knife coating, roller coating, laminating, laminating, bonding, vulcanizing, pasting and rubbing ; Solid system, poliuretan compound rubber can be vulcanized and laminated with mold, poliuretan thermoplastic can be used with thermoplastic, hot injection, calendering, blow molding, spinning and lamination.
1.3 Prinsip pencocokan tipe dasar dan metode pemrosesan cetakan
Poliuretanelastomer adalah polimer tinggi antara plastik dan karet dalam hal modulusnya. Ini terutama mencakuppoliuretan compound rubber, poliuretan cast rubber, poliuretan water emulsion and poliuretan thermoplastic. Poliuretan leather, poliuretan adhesives, poliuretan coatings, poliuretan compounds, poliuretan casting glues, poliuretan fibers, poliuretan water emulsions and poliuretan thermoplastics are all derived from the above four types of glue. The molding and processing methods of poliuretan compound rubber, poliuretan water emulsion and poliuretan thermoplastic generally belong to the molding processing methods of rubber, coatings and plastics.
1.4 The use of poliuretan elastomers and the matching principle of production continuity and molding processing methods
Poliuretan elastomer molding and processing methods are matched with the use of poliuretan elastomers, taking into account the continuity of production. For example, poliuretan leather molding methods usually use poliuretan casting adhesive or foaming layer, poliuretan water emulsion and poliuretan thermoplastic as the surface layer; also available Poliuretan thermoplastic and poliuretan water emulsion are used as leather separately, which are based on the basic rubber molding processing method, supplemented by foam molding processing, usually calender molding processing method is selected. Poliuretan paving materials are made of poliuretan casting glue, mainly due to the large product shape and low precision requirements. Medical poliuretan materials have good chemical stability, tissue compatibility, and resistance to biological aging, so the molding process uses dip coating, pouring and coating methods.